Multilayer Chip Inductors High Frequency

YAGEO CORPORATION SMD INDUCTOR / BEADS www.DataSheet4U.com Multilayer Chip Inductors High Frequency CLH/LCN Series APPLICATIONS High frequency circuits for portable telephones, PHS, Wireless communication, etc. CLH Series OUTLINE LCN Series Chilisin high frequency multilayer ceramic chip inductor is formed without wound wire. Monolithic laminated structure. FEATURES High Frequency High Q High IDC SHAPES AND DIMENSIONS Dimensions : mm Polarity Mark Terminal Electrode TYPE C REMARK – – < 180nH ≥180nH A 1.00 ± 0.15 1.60 ± 0.20 2.00 ± 0.20 2.00 ± 0.20 B 0.50 ± 0.15 0.80 ± 0.15 1.25 ± 0.20 1.25 ± 0.20 C 0.50 ± 0.15 0.80 ± 0.15 0.90 ± 0.20 1.20 ± 0.30 D 0.25 ± 0.15 0.40 ± 0.20 0.50 ± 0.30 0.50 ± 0.30 CLH1005 CLH1608 D A D B CLH2012 50 www.DataSheet4U.com ELECTRICAL CHARACTERISTICS CLH1005T SERIES PART NO. INDUCTANCE TOLERANCE at 100MHz (nH) -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S 1.0 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 15 18 22 27 33 39 47 56 68 82 100 120 150 180 220 270 330 390 470 – S = ± 0.3nH S S S S S S S, K S, K S, K S, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J = ± 5% K = ± 10% Q Min. at 100MHz 8 8 8 8 8 8 8 8 8 8 8 8 8 8 8 8 8 8 8 8 8 8 Q TYPICAL at 100MHz 9 9 10 10 10 11 11 11 11 11 11 12 12 12 12 12 12 12 10 10 9 10 at 800MHz 28 28 28 28 29 30 30 31 31 31 33 32 32 31 30 29 28 27 25 25 22 21 S.R.F TYPICAL (MHz) 6000 6000 6000 6000 6000 6000 5200 5150 4800 4100 3800 3500 3300 2600 2300 2050 1900 1700 1550 1450 1300 1250 RDC Max. (Ω) 0.10 0.10 0.10 0.10 0.12 0.12 0.15 0.15 0.18 0.20 0.25 0.25 0.30 0.30 0.40 0.50 0.60 0.70 1.50 1.80 2.00 2.00 IDC (mA) CLH1005T-1N0 CLH1005T-1N2 CLH1005T-1N5 CLH1005T-1N8 CLH1005T-2N2 CLH1005T-2N7 CLH1005T-3N3 CLH1005T-3N9 CLH1005T-4N7 CLH1005T-5N6 CLH1005T-6N8 CLH1005T-8N2 CLH1005T-10N CLH1005T-12N CLH1005T-15N CLH1005T-18N CLH1005T-22N CLH1005T-27N CLH1005T-33N CLH1005T-39N CLH1005T-47N CLH1005T-56N CLH1005T-68N CLH1005T-82N CLH1005T-R10 CLH1005T-R12 CLH1005T-R15 CLH1005T-R18 CLH1005T-R22 CLH1005T-R27 CLH1005T-R33 CLH1005T-R39 CLH1005T-R47 Note : 300 300 300 300 300 300 300 300 300 300 300 300 300 300 300 300 300 300 200 200 200 200 Tolerance : Test Conditions : L/Q – HP4291A SRF – HP8753D RDC – HP4338B Fixture – HP16193A 51 www.DataSheet4U.com ELECTRICAL CHARACTERISTICS CLH1608T SERIES PART NO. INDUCTANCE TOLERANCE at 100MHz (nH) -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S 1.0 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 15 18 22 27 33 39 47 56 68 82 100 120 150 180 220 270 330 390 470 ** at 300MHz – S = ± 0.3nH S S S S S S S, K S, K S, K S, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K * at 500MHz J = ±5% K = ±10% Q Min. at 100MHz 10 10 10 10 11 11 11 11 11 11 11 11 11 13 13 13 15 15 15 15 15 15 15 15 15 *** 8 *** 8 *** 8 *** 8 Q TYPICAL at 100MHz 12 13 13 13 13 13 13 13 13 13 13 13 13 15 15 15 17 17 18 18 18 18 18 18 18 *** 16 *** 14 *** 14 *** 13 at 800MHz 50 65 47 51 46 45 51 52 41 41 44 44 45 46 48 48 45 43 39 * 37 * 35 * 32 * 34 * 32 * 20 ** 23 ** 23 ** 21 ** 20 S.R.F TYPICAL (MHz) 6000 6000 6000 6000 6000 6000 5900 5600 4800 4350 3750 3300 2850 2500 2150 2100 1850 1680 1580 1400 1200 1100 1050 900 850 680 620 540 450 RDC Max. (Ω) 0.10 0.10 0.10 0.10 0.10 0.10 0.12 0.14 0.16 0.18 0.22 0.24 0.26 0.28 0.32 0.35 0.40 0.45 0.55 0.60 0.70 0.75 0.85 1.00 1.20 1.60 2.00 2.40 2.80 IDC (mA) CLH1608T-1N0 CLH1608T-1N2 CLH1608T-1N5 CLH1608T-1N8 CLH1608T-2N2 CLH1608T-2N7 CLH1608T-3N3 CLH1608T-3N9 CLH1608T-4N7 CLH1608T-5N6 CLH1608T-6N8 CLH1608T-8N2 CLH1608T-10N CLH1608T-12N CLH1608T-15N CLH1608T-18N CLH1608T-22N CLH1608T-27N CLH1608T-33N CLH1608T-39N CLH1608T-47N CLH1608T-56N CLH1608T-68N CLH1608T-82N CLH1608T-R10 CLH1608T-R12 CLH1608T-R15 CLH1608T-R18 CLH1608T-R22 CLH1608T-R27 CLH1608T-R33 CLH1608T-R39 CLH1608T-R47 Note : 500 500 500 500 500 500 500 500 500 500 500 500 400 400 400 400 400 400 400 300 300 300 300 300 300 250 250 200 200 *** at 50MHz Tolerance : Test Conditions : L/Q – HP4291A SRF – HP8753D RDC – HP4338B Fixture – HP16193A 52 www.DataSheet4U.com ELECTRICAL CHARACTERISTICS CLH2012T SERIES PART NO. INDUCTANCE TOLERANCE at 100MHz (nH) -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S -S 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 15 18 22 27 33 39 47 56 68 82 100 * 120 * 150 * 180 * 220 * 270 * 330 * 390 * 470 S S S S S, K S, K S, K S, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K J, K 11 11 11 11 13 13 13 13 13 13 14 14 15 15 15 16 17 19 19 16 19 20 21 * 13 * 13 * 13 * 12 * 12 * 12 * 10 * 10 13 13 13 13 15 15 15 15 15 15 16 16 17 17 17 18 19 21 21 21 21 22 23 22 22 23 20 20 22 17 17 40 45 48 40 56 54 50 53 51 53 45 48 48 43 47 38 35 40 38 31 28 16 6000 6000 6000 6000 6000 5400 4500 4000 3650 3000 2500 2450 2000 1750 1700 1550 1350 1300 1200 1150 1000 850 730 650 550 500 450 400 380 330 300 0.10 0.10 0.10 0.10 0.13 0.15 0.20 0.23 0.25 0.28 0.30 0.35 0.40 0.45 0.50 0.55 0.60 0.65 0.70 0.75 0.80 0.90 1.00 1.20 1.40 1.60 1.80 2.00 3.00 3.50 4.00 500 500 500 500 500 500 500 500 500 500 500 400 400 400 400 400 400 400 400 400 400 400 400 300 300 300 300 300 300 300 300 Q Min. at 100MHz Q TYPICAL at 100MHz at 800MHz S.R.F TYPICAL (MHz) RDC Max. (Ω) IDC (mA) CLH2012T-1N0 CLH2012T-1N2 CLH2012T-1N5 CLH2012T-1N8 CLH2012T-2N2 CLH2012T-2N7 CLH2012T-3N3 CLH2012T-3N9 CLH2012T-4N7 CLH2012T-5N6 CLH2012T-6N8 CLH2012T-8N2 CLH2012T-10N CLH2012T-12N CLH2012T-15N CLH2012T-18N CLH2012T-22N CLH2012T-27N CLH2012T-33N CLH2012T-39N CLH2012T-47N CLH2012T-56N CLH2012T-68N CLH2012T-82N CLH2012T-R10 CLH2012T-R12 CLH2012T-R15 CLH2012T-R18 CLH2012T-R22 CLH2012T-R27 CLH2012T-R33 CLH2012T-R39 CLH2012T-R47 Note : * at 50MHz Tolerance : – S = ± 0.3nH J = ± 5% K = ± 10% Test Conditions : L/Q – HP4291A SRF – HP8753D RDC – HP4338B Fixture – HP16193A 53 www.DataSheet4U.com TAPE DIMENSIONS Dimensions : mm 4±0.1 2±0.05 1.75±0.1 K±0.05 TYPE CLH1005 A 0.65 1.1 < 180nH 1.42 ≥ 180nH 1.42 B 1.15 1.9 2.25 2.25 K0 0.6 0.95 1.04 1.4 W 8 8 8 8 P 2 4 4 4 F 3.5 3.5 3.5 3.5 K 0.6 0.95 0.22 0.22 W±0.2 F±0.05 B±0.1 CLH1608 A±0.1 P±0.1 K0±0.05 CLH2012 REEL DIMENSIONS Dimensions : mm D±0.5 2±0.5 1.0 13±0.5 B±1 TYPE CLH1005 CLH1608 CLH2012 09 12 A 178 178 178 178 B 60 60 60 60 C 12 12 12 12 D 1.5 1.5 1.5 1.5 21±0.8 A±2 C±1 RECOMMENDED PATTERN B Dimensions : mm TYPE A C A 0.4 0.8 09 12 1.2 1.2 B 1.2 ~ 1.4 2.4 ~ 3.4 3.0 ~ 4.0 3.0 ~ 4.0 C 0.4 0.6 1.0 1.0 CLH1005 CLH1608 CLH2012 Solder Land Inductor TAPE MATERIAL Carrier Tape : Polystyrene Cover Type : Polyethyiene PACKAGING QUANTITY TYPE CLH100505 CLH160808 160mm Min. Blank Part Cover Tape Chip Mounting Part Blank 330mm Min. Leader BULK √ √ √ √ CHIP/REEL 10000 4000 4000 3000 CLH201209 CLH201212 54 www.DataSheet4U.com CLH SERIES RELIABILITY TEST NO 1 ITEM Bending Strength SPECIFICATION Appearance : No Damage L Change : Within ± 10% Q Change : Within ± 30% RDC Change : Within ± 20% 2 Vibration TEST METHODS Test Device shall be Soldered on the Substrate. Substrate Dimension : 95 x 23 x 1.5 mm Deflection : 2.0 mm Keeping Time : 30 Second Test Device shall be Soldered on the Substrate. 1.6 2 45 45 Oscillation Frequency : 10 to 55 to 10Hz for 1Min Amplitude : 1.5 mm 20 Time : 2 Hours for Each Axis (X, Y & Z), Total 6 Hours 3 Resistance to Soldering Heat Pre-heating : 150°C, 1 Min Solder Composition : Sn/Pn = 60/40 Solder Temperature : 260 ± 5°C Immersion Time : 10 ± 1°C Measured after Exposure in the Room Condition for 24 Hours 4 Solderability The electrodes shall be at least 90% covered with new solder coating. Pre-heating : 150°C, 1 Min Solder Composition : Sn/Pn = 60/40 Solder Temperature : 230 ± 5°C Immersion Time : 4 ± 1°C 5 Temperature Cycle Appearance : No Damage L Change : Within ± 10% Q Change : Within ± 30% RDC Change : Within ± 20% Step 1 2 3 4 Temperature (°C) -55 ± 3 25 ± 2 125 ± 2 25 ± 2 Time (Min.) 30 3 30 3 Total : 100 Cycles Measured after Exposure in the Room Condition for 24 Hours 6 Humidity Resistance Temperature : 40 ± 2°C Relative Humidity : 90 ~ 95% Time : 1000 Hours Measured after Exposure in the Room Condition for 24 Hours 7 Heat Life Temperature : 125 ± 2°C Relative Humidity : 20% Applied Current : Rated Current Time : 1000 Hours Measured after Exposure in the Room Condition for 24 Hours 8 Cold Resistance Temperature : -55 ± 3°C Time : 1000 Hours Measured after Exposure in the Room Condition for 24 Hours Storage Temperature : -55°C ~ 100°C Operating Temperature : -40°C ~ 100°C 55 www.DataSheet4U.com TYPICAL ELECTRICAL CHARACTERISTICS Test Instruments : HP4291A Impedance / Material Analyzer CLH1005T-1N0S-S 1.2 1.0 0.8 Ls (nH) CLH1005T-1N2S-S CLH1005T-1N5S-S 60 60 50 40 Ls (nH) Q 1.2 1.0 2 80 1.5 0.8 0.6 0.4 0.2 1 1 10 100 1000 FREQUENCY (MHz) 0 20 40 Ls (nH) Q 60 0.6 0.4 0.2 0 1 10 100 1000 FREQUENCY (MHz) 30 20 10 0 1 40 0.5 20 0 1 10 100 1000 FREQUENCY (MHz) 0 RDC: 0.10Ω IDC: 300mA Frequency: 100MHz OSC: 500mV SRF: 6000MHz RDC: 0.10Ω IDC: 300mA Frequency: 100MHz OSC: 500mV SRF: 6000MHz RDC: 0.10Ω IDC: 300mA Frequency: 100MHz OSC: 500mV SRF: 6000MHz CLH1005T-1N8S-S 2 80 2.5 2 CLH1005T-2N2S-S 50 40 CLH1005T-2N7S-S 3 2.5 2 60 50 40 30 20 10 1 10 100 1000 FREQUENCY (MHz) 0 Q Q Q Q 1.5 60 Ls (nH) Ls (nH) 1 40 Ls (nH) 1.5 1 0.5 0 30 Q Q 1.5 1 20 10 0 0.5 20 0.5 1 0 1 10 100 1000 FREQUENCY (MHz) 0 1 10 100 1000 FREQUENCY (MHz) RDC: 0.10Ω IDC: 300mA Frequency: 100MHz OSC: 500mV SRF: 6000MHz RDC: 0.12Ω IDC: 300mA Frequency: 100MHz OSC: 500mV SRF: 6000MHz RDC: 0.12Ω IDC: 300mA Frequency: 100MHz OSC: 500mV SRF